Light Weight Mullite Refractory Bricks with Hole

• Customization: Available
• Refractoriness (℃): 1580< Refractoriness< 1770
• Feature: Long Time Materials
• Model NO.: WAM C3
• Shape: Brick
• Material: Alumina
• Size: According to The Requirements
• Transport Package: on Pallet
• Specification: ISO9001: 2015
• Trademark: WAM
• Origin: Qingdao, China
• HS Code: 69022000
• Production Capacity: 8, 000, 000/Year

Product Description

WAM Series Insulating Bricks
WAM series insulating bricks are a kind of highly efficient, energy saving, low-carbon, environmental protection advanced products
which are manufactured according to ASTM standard. WAM series products are the best lining and insulation materials in all types
of industrial furnaces in the field of Metallurgy, Aluminum, Petrochemical, Ceramics, Power and Glass. They can be applied as heat
insulation or no-melt erosion parts of the working layer. The products have been widely used in the following furnaces and achieved
satisfactory results.

Metallurgy industry: Blast furnace, Hot blast stove, Reheating furnace, etc.
Petrochemical industry: Ethylene cracking furnace, Hydrogen production furnace, Primary reformer furnace, Reheating furnace, etc.
Ceramics Industry: Roller kiln, Pusher kiln, etc.
Glass industry: Glass furnace regenerator, etc.
Carbon Industry: Carbon roaster, etc.
Aluminum electrolytic industry: Aluminum reduction cells, etc.
Other industries: Tunnel kiln, Shuttle kiln, etc.

Advantages
Low Thermal Conductivity: More porosity brings excellent insulation effect, energy saving.
High Crushing Strength: High crushing strength under thermal state, volume stability.
Low Heat Storage: Little thermal storage when absorb more heat, energy saving effect is obvious.
High Purity: Low content of iron, alkaline and metal impurities.
Accurate Dimension: Precise brick size by machining, cutting and grinding special shapes, expediting bricklaying.

Physical and Chemical Properties of insulating  brick
Index /brand		WAM-20	WAM-23	WAM-25	WAM-26	WAM-28	WAM-30	WAM-32
Classification temperature   ºC		1230	1260	1350	1430	1540	1650	1760
F		2246	2300	2462	2606	2804	3002	3200
Bulk density   kg/m 3		520	580	800	800	890	1030	1250
Ib/ft 3		32	36	50	50	55.5	64	78
Modulus of rupture   MPa		0.7	0.9	1.4	1.5	1.6	1.7	2
Ib/in 2		102	131	203	218	232	247	290
Cold crushing strength  MPa		1.2	1.2	2.0	2.0	2.6	2.8	3.4
Ib/in 2		174	174	363	348	377	406	493
Permanent Liner Change  %		-0.1	-0.1	-0.5	-0.5	-0.8	-0.9	-0.9
o C x hour		1230X24	1230X24	1350X24	1400x24	1510x24	1620x24	1730x24
	400 ºC	0.17	0.17	0.24	0.24	0.30	0.40	0.49
Thermal conductivity	600 ºC	0.19	0.19	0.28	0.27	0.32	0.42	0.50
(W/m. k)	800 ºC	0.22	0.22	0.32	0.30	0.35	0.44	0.51
	1000 ºC	0.24	0.25	0.37	0.32	0.38	0.45	0.53
	1200 ºC	--	--	--	0.35	0.39	0.47	0.55
Al2O3    %		45	45	45	55	65	72	76
Fe2O3      %		0.7	0.7	0.65	0.6	0.3	0.3	0.3
SiO2    %		50	50	50	42	33	26	22
TiO2   %		1.3	1.2	1.3	1.1	0.9	0.5	0.3
CaO+ MgO  %		0.5	0.7	0.6	0.3	0.2	0.3	0.2
K2O+ Na2O  %		1.0	1.3	1.1	1.1	0.8	0.2	0.1
The above datas are subject to normal manufacturing variations and change without notice. Results should not be used for specification purpose.